C95510 / AMS 4880 is one of the most popular landing gear bushing materials specified today along with C63000 material. This continuous / centrifugal cast alloy is heat treated and exhibits high mechanical strength which meets the properties of C63000 (AMS 4640). In many cases C95510 (AMS 4880) can be substituted for C63000 with the advantage of this material being available in hollow bar, which provides economic cost savings for you, the customer.

Typical Uses for C95510 Nickel Aluminum Bronze

AEROSPACE: Landing Gear Bushings & Bearings, Valve Guides, Stems, Seats

INDUSTRIAL: Corrosion Resistant Parts, Wear Rings, Machine Tool Parts, Piston Guides, Worm Wheels, Hot Mill Gurdes

MARINE: Propeller Hubs, Wear Rings, Hardware, Worm Gears, Shafts, Sleeves

Sizes Available From NBM

SOLID BAR: 1/2" - 12" diameter

HOLLOW BAR (Continuous Cast): thru 10" diameter

C95510 Alloy Specifications

Product Type Temper Type Centrifugal ASTM B271, SAE J462, J461, AMS 4880 Continuous ASTM B505, SAE J462, J461, AMS 4880 Ingot ASTM B30 Precision ASTM B806 Sand ASTM B148, B763, SAE J461, J462

Chemical Composition

The following table shows the chemical composition of copper UNS C95510.

Element Content (%) Cu% 78.00-min Sn% 0.20 Zn% 0.30 Fe% 2.00-3.50 Ni% 4.50-5.50 Al% 9.70-10.90 Mn% 1.50

Physical Properties

The physical properties of copper UNS C95510 are outlined in the following table.

Properties Metric Imperial Density 7.58 g/cm³ 0.274 lb/in³ Melting point 1035°C 1895°F

Mechanical Properties

The mechanical properties of copper UNS C95510 are tabulated below.

Properties Metric Imperial Tensile strength 780 MPa 110000 psi Yield strength  490 MPa 68200 psi Elongation at break (in 50 mm, 10% reduction in area) 15% 15% Elastic modulus 117 GPa 17000 ksi Poisson's ratio 0.34 0.34 Reduction of area (at 316°C/601°F, cold finished) 9% 9% Shear modulus 44.0 GPa 6380 ksi Fatigue strength (at number of cycles 1.00e+8, reverse bending) 255 MPa 37000 psi Hardness, Rockwell B 94 94 Machinability (UNS C36000 (free-cutting brass) = 100) 30 30